The effect of cooling procedures on monomer elution from heat-cured polymethyl methacrylate denture base materials

Abstract Objective To evaluate the amount of methyl methacrylate (MMA) released in water from heat-cured polymethyl methacrylate (PMMA) denture base materials subjected to different cooling procedures. Methodology Disk-shaped specimens (Ø:17 mm, h:2 mm) were fabricated from Paladon 65 (PA), ProBase Hot (PB), Stellon QC-20 (QC) and Vertex Rapid Simplified (VE) denture materials using five different cooling procedures (n=3/procedure): A) Bench-cooling for 10 min and then under running water for 15 min; B) Cooling in water-bath until room temperature; C) Cooling under running water for 15 min; D) Bench-cooling, and E) Bench-cooling for 30 min and under running water for 15 min. A, B, D, E procedures were proposed by the manufacturers, while the C was selected as the fastest one. Control specimens (n=3/material) were fabricated using a long polymerization cycle and bench-cooling. After deflasking, the specimens were ground, polished and stored in individual containers with 10 ml of distilled water for seven days (37oC). The amount of water-eluted MMA was measured per container using isocratic ultra-fast liquid chromatography (UFLC). Data were analyzed using Student's and Welch's t-test (α=0.05). Results MMA values below the lower quantification limit (LoQ=5.9 ppm) were registered in B, C, E (PA); E (PB) and B, D, E (QC) procedures, whereas values below the detection limit (LoD=1.96 ppm) were registered in A, D (PA); A, B, C, D (PB); C, D, E (VE) and in all specimens of the control group. A, B (VE) and A, C (QC) procedures yielded values ranging from 6.4 to 13.2 ppm with insignificant differences in material and procedure factors (p>0.05). Conclusions The cooling procedures may affect the monomer elution from denture base materials. The Ε procedure may be considered a universal cooling procedure compared to the ones proposed by the manufacturers, with the lowest residual monomer elution in water.

Removal of denture adhesives from PMMA and Polyamide denture base materials

Abstract Denture adhesives need complete removal due to their frequent replacement. Objective Our study investigates the removal of denture adhesives from denture base materials, using different methods. Methodology PMMA and Polyamide denture base materials were used to fabricate 120 samples (15×15×1.5mm). One side of the samples was left as processed and the other polished with a usual procedure, hydrated for 24 h, dried, and weighted. They received 0.2 g of three adhesive creams on their unpolished surface (Corega, Olivafix, Fittydent), pressed on polysulfide material, stored under 37°C and 95% rel. humidity for 1 h and 60 of them, following their separation from polysulfide base, brushed under running water, whereas the rest inserted in a cleanser bath (Fittydent Super) for 5 min. The samples were dried and inserted in the oven (37°C) for additional 10 min and weighted again. Roughness tests of denture materials and light microscopy of adhesives creams were also used to evaluate the materials. Time lapse images of spayed with water adhesives on PMMA base were also taken to evaluate the volumetric changes of adhesives. Weight data before and after adhesive removal, indicating the amount of remaining adhesive, were statistically analyzed using Welch's ANOVA and Games-Howell multiple comparisons tests at α=0.05 level of significance. Results Roughness of Polyamide was higher than PMMA and Fittydent showed greater volumetric changes than the others. Significant differences (p<0.05), were found between PMMA and Polyamide bases, between Olivafix and Fittydent adhesives, and between brushing and cleansing methods but only for PMMA-Olivafix combination. Conclusions Adhesives showed a stronger adherence to PMMA surface, and Fittydent was the most difficult to be removed. Removal methods were not effective for all adhesives or denture base materials. These indicate that removal methods, adhesive type and denture base material are all playing a significant role in the removal of adhesives from denture surfaces.

Intra- and inter-brand color differences of denture teeth under different illuminations

Abstract Debonding, staining and wear are usually the reasons for denture teeth replacement by new ones from same or different brands. Objective This study investigates the possible differences in color of denture teeth of the same or different brands under different illuminations, since their metameric behavior in color under specific illumination may become unacceptable. Methodology For the purpose of this study, 10 denture teeth (#11), shade A3, of 4 different brands were selected (Creopal/KlemaDental Pro, Executive/DeguDent, Cosmo HXL/DeguDent, Ivostar/Ivoclar-Vivadent). Teeth stabilized in white silicone mold and the CIELAB color coordinates of their labial surface under 3 different illumination lights (D65, F2, A) were recorded, using a portable colorimeter (FRU/WR-18, Wave Inc). ΔE*ab values of all possible pairs of teeth of the same brand (n=45) or pair combinations of different brands (n=100) under each illumination light, in a dry and wet state were calculated. Data were analyzed statistically using 3-way ANOVA, Friedman's and Wilcoxon's tests at a significance level of α=0.05. Results The results showed that brand type affected significantly L*, a* and b* coordinates (p<0.0001), illumination a* and b* coordinates (p<0.0001), but none of them was affected by the hydration state of teeth (p>0.05). Intra-brand color differences ranged between 0.21-0.78ΔΕ* units with significant differences among brands (p<0.0001), among illumination lights (p<0.0001) and between hydration states (p=0.0001). Inter-brand differences ranged between 2.29-6.29ΔΕ* units with significant differences among pairs of brands (p<0.0001), illumination lights (p<0.0001) and hydration states (p<0.0001). Conclusions Differences were found between and within brands under D65 illumination which increased under F2 or A illumination affected by brand type and hydration status. Executive was the most stable brand than the others under different illuminations or wet states and for this reason its difference from other brands is the lowest. In clinical practice, there should be no blending of teeth of different brands but if we must, we should select those that are more stable under different illuminations

Long-term microwaving of denture base materials: effects on dimensional, color and translucency stability

Abstract While the combined effect of microwave irradiation with cleansing solutions on denture base materials has been investigated, the effects of only using microwave irradiation and, more importantly, in a long-term basis, was not studied yet. Objective The purpose of this study was to evaluate the effect of a long-term repeated microwaving on the dimensional, color and translucency stability of acrylic and polyamide denture base materials. Material and Methods Thirty two specimens (32 mm x 10 mm x 2.5 mm) from polyamide (Valplast) and PMMA (Vertex Rapid Simplified) denture base materials were made. Eight specimens from each material were immersed in distilled water (control) and 8 were subjected to microwave exposure at 450 W for 3 minutes for a period simulating 224 days of daily disinfection. Linear dimension, color change (ΔE*) and translucency parameter (TP) were measured at baseline and after certain intervals up to 224 cycles of immersion, using a digital calliper and a portable colorimeter. The results were analysed using two-way repeated measures ANOVA to estimate possible differences among predetermined cycles and material type. Regression analysis was also performed to estimate the trend of changes with time. Statistical evaluations performed at a significance level of 5%. Results Data analysis showed significant changes in length at baseline with an increasing number of cycles (p<0.05) and a significant interaction of cycle-material (p<0.001). The ΔΕ* parameter was significantly higher with a higher number of cycles (p<0.001), but it did not vary between materials (p>0.05). TP decreased similarly in both materials following microwave action but in a significantly higher level for Valplast (p<0.001). Conclusions The results indicated that long-term repeated microwaving affects linear dimensional, color and translucency changes of both materials. Differences between PMMA and polyamide material were noted only in dimension and translucency changes.

Effect of different disinfecting procedures on the hardness and color stability of two maxillofacial elastomers over time

Objective Disinfection procedures often cause deterioration in a maxillofacial prosthesis. Color and hardness alterations could lead to a replacement of the prosthesis. Material and Methods An experimental chlorinated polyethylene (CPE) and a commercial polydimethyl siloxane (PDMS) sample were treated with four different disinfection procedures for a period which simulates 1 year of clinical service. The applied disinfection procedures included microwave exposure and immersion in three solutions, sodium hypochlorite, neutral soap and a commercial disinfecting soap. Shore A hardness (∆H) and color differences (∆E) were determined before and after each procedure. All data were analyzed by Two Way Analysis of Variance (ANOVA) and Tukey's post hoc tests at a level of α=0.05. Results The samples presented significant alterations in color and hardness after the different disinfection treatments. The color differences (∆E) were at least eye detectable in all cases and clinically unacceptable in most of the cases, with values ranging from 1.51 to 4.15 and from 1.54 to 5.92 for the PDMS and CPE material, respectively. Hardness was decreased after all the disinfection procedures in the PDMS, while for the CPE, a decrement was observed after disinfection with sodium hypochlorite and neutral soap and an increment after microwave exposure and the disinfection with a commercial antimicrobial agent. The PDMS samples presented greater alterations in color and hardness after disinfection with sodium hypochlorite solution, while the microwave exposure caused negligible effects. The CPE samples were affected most after disinfection when treated with neutral soap, and more slightly when disinfected with sodium hypochlorite solution. Conclusions The disinfection procedures caused alterations in color and hardness of the examined materials. The most suitable disinfection procedure for ...

Effectiveness of mechanical brushing with different denture cleansing agents in reducing in vitro Candida albicans biofilm viability

The adhesion of Candida albicans to surfaces is the prerequisite for occurrence of denture stomatitis, a common disease diagnosed among denture wearers. A routine of denture cleansing is essential to prevent biofilm formation and the onset of this infection. The aim of this study was to investigate the effectiveness of combining brushing and cleansing agents in killing C. albicans biofilm. Disks of acrylic resin were made, sterilized, and inoculated with C. albicans (10(7) cfu/mL). After incubation (37°C/48 h), specimens were randomly assigned to 10 experimental groups (n=9): 5 subjected to brushing with distilled water or cleansing agents - dentifrice slurry, 2% chlorhexidine gluconate (CHX), 1% sodium hypochlorite (NaOCl), and Polident fresh cleanse® (combined method) - and 4 exposed to the cleansing agents without brushing (immersion). Non-cleansed specimens were used as positive controls. The viability of cells was evaluated by XTT reduction method. Results were analyzed by Mann-Whitney and Kruskal-Wallis tests (α=0.05). The combined method was significantly more effective (p<0.0001) in reducing biofilm viability than the immersion. Brushing with CHX and NaOCl resulted in 100% removal of the biofilm. Immersion in the agents reduced significantly (p<0.0001) the biofilm viability, with CHX being the most effective (p<0.0001). The use of the combined method of brushing with cleansing agents is an effective method to reduce C. albicans biofilm, being CHX and NaOCl the most effective solutions.

A adesão de Candida albicans às superfícies é o primeiro passo para o desenvolvimento da estomatite protética, uma infecção frequente diagnosticada entre os usuários de próteses. Uma adequada higienização é essencial para prevenir a formação de biofilme microbiano e o início desta infecção. O objetivo deste estudo foi avaliar a efetividade da escovação com diferentes soluções na eliminação de biofilme de C. albicans. Para isso, discos de resina acrílica foram confeccionados, esterilizados e inoculados com uma suspensão de 10(7) células/mL de C. albicans. Após incubação (37°C/48 h), os espécimes foram aleatoriamente divididos em 10 grupos experimentais (n=9): 5 submetidos à escovação com água ou agentes de limpeza (água destilada, dentifrício, digluconato de clorexidina (CHX) a 2%, hipoclorito de sódio (NaOCl) a 1% e Polident fresh cleanse®) e 4 apenas imersos nos agentes de limpeza. Espécimes não submetidos à higienização foram utilizados como controle positivo. A viabilidade celular foi verificada pelo teste de redução do XTT. Os resultados obtidos foram analisados pelos testes de Mann-Whitney e Kruskal-Wallis (α=0,05). A escovação com todos os agentes de limpeza apresentou redução significativamente superior (p<0,0001) na viabilidade do biofilme quando comparada à exposição dos espécimes às soluções. Escovação com CHX a 2% e NaOCl a 1% resultaram em 100% de inativação do biofilme. A exposição aos agentes de limpeza resultou em redução significativa (p<0,0001) na viabilidade celular, com CHX a 2% sendo o mais efetivo (p<0,0001). A utilização de agentes de limpeza em associação ao método de escovação provou ser efetivo para reduzir biofilme C. albicans, sendo as soluções de CHX e NaOCl as mais efetivas.